Resin SZUV-T1120-elu okpom?k? na-eguzogide
Okwu mmalite
Njirimara:
SZUV -T1120 b? resin SL edo edo nke nwere ar?m?r? ?k? na-enwegh? at?. ? nwere ike idi okpom?k? kar?a 200 ℃ na obere oge na 120 ℃ na ogologo oge. Emebere ya maka ijikwa ?d? okpom?k? d? iche iche na ngwa nnwale ?j??.
At?mat? ah?kar?
IKE d? elu na EZIGBO eguzogide
SZUV-T1120 nwere ike iguzo iru mmiri, mmiri na ihe mgbaze, d? ka mman? ?gb?ala, nnyefe mmiri mmiri, mman? na coolant. Site na nguzogide okpom?k? ya na-enwegh? at?, ? dabara adaba maka ?gbasa, HVAC, ?k?, ngwá ?r?, ?kp?zi na ngwa nyocha ?wara ikuku.
-wulite ngwa ngwa ma z?lite ngwa ngwa
Site n'inye ngwa ngwa ngwa ngwa na ak?k? na elu d? lar??, d? mfe ijikwa, SZUV-T1120 nwere ike imecha ?r? g? site na ?b?aru na ak?k? ule na obere oge.
Ngwa ngwa
-N'okpuru mkpuchi ak?r?ngwa nnwale
-Elu okpom?k? RTV ?kp?zi
-Nnwale ?wara ikuku
-Nnwale ?k? ?k?
- Ngwa ?r? autoclave mejup?tara
-Nnwale ak?r?ngwa HVAC
-Nnyocha nke ukwuu
- Orthodontics
OGE NKWUKWU
Ag?makw?kw?
Akp?kp? aka
Ak?k? akpaaka
Nkwak? ngwaah?a
Nhazi nka
?gw?
AK?R? AR? AH? (mmiri)
| ?d?d? | ?cha |
| Njup?ta | 1.13g / cm3@ 25 ℃ |
| Viscosity | 400~480 cps @ 29 ℃ |
| Dp | 0.152 mm |
| Ec | 7.6mJ/cm2 |
| ?l? oyi akwa ?kp?r?kp? | 0.05 ~ 0.12mm |
?
AKW?KW?KW?KW?KW?KW?KW?KW?KW?KW?KW?KW?KW?KW?KW?KW?KW?KW?KW?KW?KW?KW?KW?KW?KW?KW?KW?KW?KW?KW?KW?KW?KW?KW?KW?KWAS?
| Nt? | Usoro ule | Uru | |
| Ngw?ta UV nke nkeji 90 | 90-nkeji UV +2 awa @ 160 ℃ ?gw?gw? ?k? gachara | ||
| Hardness, Shore D | ASTM D2240 | 87 | 91 |
| Mgbanwe mgbanwe, Mpa | ASTM D790 | 2678-3186 | 3502-3631 |
| Ike mgbanwe, Mpa | ASTM D790 | 60-80 | 90-101 |
| modul tensile, MPa | ASTM D638 | 2840-3113 | 3484-3771 |
| Ike tensile, MPa | ASTM D638 | 58-67 | 50-62 |
| Elongation na ezumike | ASTM D638 | 4-8% | 4-6% |
| Ike mmet?ta, ?p?r?iche lzod, J/m | ASTM D256 | 18-30 | 16-23 |
| Okpom?k? ngbanwe, ℃ | ASTM D 648 @66PSI | 81 | 98 |
| Ntughar? iko, Tg, ℃ | DMA, elu | 100 | 111 |
| ?n??g? nke mgbasawanye thermal, E6/℃ | TMA (T | 79 | 86 |
| Nr?p?ta ?k?, W/m.℃ | 0.171 | ||
| Njup?ta | 1.24 | ||
| Ntinye mmiri | ASTM D 570-98 | 0.49% | 0.46% |
?
Njirimara ar?r? ar? nke ihe emechara ka emechara
| Nhazi | UZ? anwale ? | ? | URU |
| ? | ? | Ngw?ta UV nke nkeji 90 | 90 nkeji UV +2 awa @ 160℃thermalmgbe ?gw?gw? gas?r? |
| Hardness, Shore D | ASTM D2240 | 87 | 91 |
| Mgbanwe mgbanwe, Mpa | ASTM D790 | 2678-3186 | 3502-3631 |
| Ike mgbanwe, Mpa | ASTM D790 | 60-80 | 90-101 |
| modul tensile, MPa | ASTM D638 | 2840-3113 | 3484-3771 |
| Ike tensile, MPa | ASTM D638 | 58-67 | 50-62 |
| Elongation na ezumike | ASTM D638 | 4-8% | 4-6% |
| Ike mmet?ta, ?p?r?iche lzod, J/m ? | ASTM D256 ? | 18-30 ? | 16-23 |
| Okpom?k? ngbanwe,℃ ? | ASTM D 648 @66PSI ? | 81 | 98 ? |
| Ntughar? iko,Tg ,℃ | DMA,E”elu ? | 100 | 111 ? |
| ?n??g? nke mgbasawanye thermal, E6/℃ | TMA(T) ? | 79 ? | 86 ? |
| Nr?p?ta ?k?, W/m.℃ | ? | 0.171 | ? |
| Njup?ta | ? | 1.24 | ? |
| Ntinye mmiri | ASTM D 570-98 | 0.49% | 0.46% |